Sikaflex®-298 FC
Sikaflex®-298 FC is a slightly thixotropic 1-component polyurethane adhesive which cures on exposure to atmospheric humidity. It is used for Teak deck bedding. Sikaflex®-298 FC meets the regulations set out by the International Maritime Organization (IMO).
- Fast skin formation
- Slightly thixotropic
- Sound deadening properties
- Elastic behavior
- Contains no highly inflammable solvents
PRODUCT BENEFITS
- Fast skin formation
- Slightly thixotropic
- Sound deadening properties
- Elastic behavior
- Contains no highly inflammable solvents
Usage
Sikaflex®-298 FC is suitable for bonding deck covering materials made from synthetic resins (except polyethylene and polypropylene), and for bedding-in of teak plank decking laid on top of the sub deck surface. Suitable substrates include GRP, marine plywood, steel, aluminum sealed with an anti-corrosion coating (epoxy or polyurethane-acrylic based) and stainless steel. Sikaflex®-298 FC is a faster skinning version of the Sikaflex®-298. Consider the faster skinning time if used under elevated temperature and/or higher humidity.Sikaflex®-298 FC is suitable for experienced professional users only. Test with actual substrates and conditions have to be performed to ensure adhesion and material compatibility.
Packaging
| Unipack | 600 ml |
| Pail | 10 l |
Product Details
| Chemical base | 1-component polyurethane | |
| Color (CQP001-1) | Black | |
| Cure mechanism | Moisture-curing | |
| Density (uncured) | 1.2 kg/l | |
| Non-sag properties (CQP061-1) | Slightly thixotropic | |
| Application temperature | 10 ─ 35 °C | |
| Skin time (CQP019-1) | 50 minutes A | |
| Curing speed (CQP049-1) | (see diagram 1) | |
| Shrinkage (CQP014-1) | 6 % | |
| Shore A hardness (CQP023-1 / ISO 48-4) | 25 | |
| Tensile strength (CQP036-1 / ISO 527) | 1.2 MPa | |
| Elongation at break (CQP036-1 / ISO 527) | 400 % | |
| Tear propagation resistance (CQP045-1 / ISO 34) | 4 N/mm | |
| Service temperature (CQP509-1 / CQP513-1) | -50 ─ 90 °C | |
| Shelf life (CQP016-1) | unipack pail | 12 months B 9 months B |
| CQP = Corporate Quality Procedure | A) 23 °C / 50 % r. h. | B) storage below 25 °C |
CURE MECHANISM
Sikaflex®-298 FC cures by reaction with atmospheric moisture. At low temperatures the water content of the air is generally lower and the curing reaction proceeds somewhat slower (see diagram 1).
Diagram 1: Curing speed Sikaflex®-298 FC
CHEMICAL RESISTANCE
Sikaflex®-298 FC is generally resistant to fresh water, seawater, diluted acids and diluted caustic solutions; temporarily resistant to fuels, mineral oils, vegetable and animal fats and oils; not resistant to organic acids, glycolic alcohol, concentrated mineral acids and caustic solutions or solvents.
Application
Surface preparation
Surfaces must be clean, dry and free from grease, oil, dust and contaminants.
Surface treatment depends on the specific nature of the substrates and is crucial for a long lasting bond. Suggestions for surface preparation may be found on the current edition of the appropriate Sika® Pre-treatment Chart. Consider that these suggestions are based on experience and have in any case to be verified by tests on original substrates.
Application
Sikaflex®-298 FC can be processed between 10 °C and 35 °C but changes in reactivity and application properties have to be considered. The optimum temperature for substrates and adhesive is between 15 °C and 25 °C. The adhesive is applied over large surface areas with a notched spreader (notch depth approx. 4 mm). The consumption is approx. 1.2 l per m2. If the substrates to be bonded are impervious to moisture or if an accelerated rate of cure is required, the adhesive could be lightly sprayed with a water mist shortly before the substrates are joined together (use an aerosol spray or spray gun to apply approx. 10 g water per m2). Avoid air entrapment when joining the parts or filling joints. Apply firm pressure when bringing components together and keep the bond under pressure for at least 3 hours until the adhesive has set.
The open time is significantly shorter in hot and humid climate. The parts must always be installed within the open time. Never join bonding parts if the adhesive has built a skin.
Removal
Uncured Sikaflex®-298 FC can be removed from tools and equipment with Sika® Remover-208 or another suitable solvent. Once cured, the material can only be removed mechanically. Hands and exposed skin have to be washed immediately using hand wipes such as Sika® Cleaner-350H or a suitable industrial hand cleaner and water. Do not use solvents on skin!