SikaForce®-472 FR L60

Non sagging structural adhesive

SikaForce®-472 FR L60 is a high viscous 2-component polyurethane adhesive for assembling sandwich panels and similar constructions of various materials.  

  • Room temperature curing
  • Highly impact resistant
  • IMO compliance acc. to DNV-GL
  • Solvent free
  • Good non-sag properties in thin adhesive layer
 
Product Data Sheet Show all documents

Product Details

Typical Product Data
Properties

Component A

SikaForce®-472 FR L60

Component B

SikaForce®-040

(formerly SikaForce®-7752 (B))

Chemical base

Polyols

Isocyanate derivatives

Color (CQP001-1)

 

mixed

White

Brown

Beige

Cure mechanism

Polyaddition

Density (uncured)

 

mixed (calculated)

1.60 g/cm3

1.23 g/cm3

1.52 g/cm3

Solid content

100 %

100 %

Mixing ratio

by volume

by weight

100 : 26

100 : 20

Viscosity (CQP029-4)

Rheometer, PP25, shear rate 10 s-1, d=0.2 mm

mixed

200 000 mPa∙s A

200 mPa∙s B

70 000 mPa∙s A

Application temperature

15 – 30 °C

Pot life (CQP536-2)

70 minutes B

Open time (CQP526-3)

85 minutes B

Press time (CQP590-4)

1 MPa

300 minutes B

Shore D hardness (CQP023-1 / ISO 868)

75 C

Tensile strength (CQP543-1 / ISO 527)

20 MPa C

Elongation at break (CQP543-1 / ISO 527)

10 % C

Tensile lap-shear strength (CQP546-1 / ISO 4587)

11 MPa C

Gross calorific potential (EN ISO 1716)

16 MJ/kg

Shelf life

12 months

9 months

CQP = Corporate Quality Procedure

A) 20 °C

B) 23 °C / 50 % r.h.

C) 12 weeks at 23 °C / 50 % r.h.

Technical Information

CURE MECHANISM

The curing of SikaForce®-472 FR L60 takes place by a chemical reaction of the two components. Higher temperatures speed up the curing process and lower slow it down.

CHEMICAL RESISTANCE

In case of chemical or thermal exposure, conduct project related testing.

Application

Application Information

Surface preparation

Surfaces must be clean, dry and free from grease, oil, dust and contaminants. After the cleaning process, a physical or chemical pre-treatment might be required, depending on surface and type of material. The type of pre-treatment must be determined by tests.

Application

Volume and positioning of the adhesive must be defined in a way, that the intended gap is sufficiently filled after joining the parts. The specific applied quantity and position must be determined by tests.
The procedure for manual application is as follows: Ensure that the A-component is stirred thoroughly to avoid any sediment or separation, taking care not to stir too vigorously as this may introduce air into the product. Add the B-component in the specified ratio and stir thoroughly, ensuring a homogeneous mixture is achieved.
Apply before reaching half of the pot-life and join parts together within the open time. Consider that, if mixed in larger amounts, the exothermic reaction can reduce the pot-life and open time significantly.
For support on selecting and setting up a suitable pump system, contact the System Engineering department of Sika Industry.

 

Pressing

An adequate bonding pressure is necessary to obtain a voidless contact between the substrates and the adhesive. The specific pressure is, however, dependent on the core material and must be determined by tests. The pressure must always be below the maximum compressive strength of the core. After starting the press process, do not release the pressure until the press time has elapsed.

Removal

Uncured SikaForce®-472 FR L60 may be removed from tools and equipment with SikaForce®-096 Cleaner (formerly SikaForce®-7260 Cleaner). Once cured, the material can only be removed mechanically.
Hands and exposed skin have to be washed immediately using hand wipes such as Sika® Cleaner-350H or a suitable industrial hand cleaner and water.

Do not use solvents on skin.

STORAGE CONDITIONS

SikaForce®-472 FR L60 has to be kept between 10 °C and 30 °C in a dry place. Do not expose it to direct sunlight or frost. After opening of the packaging, the content has to be protected against humidity.
The lowest allowed temperature during transportation is -20 °C for max. 7 days.