Product Data Sheet
Show all documents

Sika Poxicolor® SW Neu

Mechanically resistant epoxy resin coating with low solvent content

Abrasion resistant, economically 2-pack coating based on epoxy resin.
Low solvent content according to Protective Coatings Directive of German Paint Industry Association (VdL-RL 04).

  • High-build application with dry film thicknesses
    up to 200 µm per coat
  • Tough hard, abrasion resistant
  • Low solvent content
  • Suitable for cathodic protection systems
  • Quick curing
  • Tar-free
Product Data Sheet
Show all documents

Usage

Tough hard, easily applied high-build system. Corrosion protection for hydraulic steel structures (flood gates, steel sheet piles etc.), where a mechanically resistant coating is required. Also suitable as a fast curing single layer system of low solvent content for the corrosion protection of steel constructions (workshop application).  

Advantages

  • High-build application with dry film thicknesses
    up to 200 µm per coat
  • Tough hard, abrasion resistant
  • Low solvent content
  • Suitable for cathodic protection systems
  • Quick curing
  • Tar-free

Packaging

Sika Poxicolor® SW Neu15 kg net.
Sika® Thinner S25 l, 10 l and 3 l
SikaCor® Cleaner160 l and 25 l

Colour

Black, redbrown, approx. RAL 7032, approx. RAL 9002.
In case of exposure to weathering Sika Poxicolor® SW Neu tends to chalking and yellowing. In case of higher demands to colour retention, SikaCor® EG-4 or SikaCor® EG-5 respectively are recommended as top coats.

Slight colour deviations are possible due to raw material characteristics.

Product Details

Sustainability / Certifications / Approvals

CERTIFICATES AND TEST REPORTS

  • Tested and listed by the German Federal Waterways Engineering and Research Institute (BAW).
  • Tested and approved according Norsok M-501, edition 6, system no. 7A and 7B.
Product Information

Shelf life

2 years

Storage conditions

In originally sealed containers in a cool and dry environment.

Density

~1,6 kg/l

Solid content

~82 % by volume
~90 % by weight
Technical Information

Chemical resistance

Permanently resistant to industrial and marine atmosphere, water, waste water, seawater, neutral salts, mineral oils, fuels, grease, oil, detergents etc..

Temperature resistance

Dry heat up to approx. + 100°C
Damp heat and warm water up to approx. + 40°C

Application

Application Information

Mixing ratio

Components A : B

By weight90 : 10

Material temperature

Min. + 5°C

Relative air humidity

Max. 85 %, except the surface temperature is significantly higher than the dew point temperature, it shall be at least 3 K above dew point.

The surface must be dry and free from ice.

Pot Life

At + 20°C~1 h
At + 30°C~45 min.

Waiting time to overcoating

Min.: until drying stage 6 is achieved (see above table)

Max.: 3 months

In case of longer waiting times please contact us.

Thinner

Sika® Thinner S
If necessary max. 3 % Sika® Thinner S may be added to adapt the viscosity.

Drying time

Final drying time
At + 20°C final hardness is achieved within 1 week.

 

Drying stage 6

Dry film thickness 200 µm
+ 5 °C after30 h 
+ 10 °C after20 h
+ 20 °C after8 h
+ 40 °C after3 h

Surface temperature

Min. 0°C
Consumption

Consumption

Theoretical material-consumption/coverage without loss for medium dryfilm thickness:

Dry film thickness200 µm

Wet film thickness

245 µm

Consumption

~0.390 kg/m²
Converage~2.60 m²/kg
Application steps

MIXING

Stir component A very thoroughly using an electric mixer (start slowly, then increase up to approx. 300 rpm). Add component B carefully and mix both components very thoroughly (including sides and bottom of the container). Mix for at least 3 minutes until a homogeneous mixture is achieved. Fill mixed material into clean container and mix again shortly as described above. During mixing and handling of the materials always wear protective goggles, suitable gloves and other protective clothings.

APPLICATION

The method of application has a major effect on achieving uniform thickness and appearance. Spray application will give the best results. The indicated dry film thickness is easily achieved by airless spray. Adding solvents reduces the sag resistance and the dry film thickness.

 

In case of application by roller or brush, additional applications may become necessary to achieve the required coating thickness, depending on type of construction, site conditions, colour shade etc. Prior to major coating operations a test application on site may be useful to ensure the selected application method will provide the requested results.

By brush and roller

Airless-spraying:

  • Efficient airless equipment
  • Pressure min. 180 bar
  • Nozzle size 0.43 - 0.53 mm (0.017 - 0.021 inch)
  • Spraying angle 40° - 80°
  • Diameter of hoses min. 10 mm (⅜ inch)

CLEANING OF EQUIPMENT

SikaCor® Cleaner