Sikafloor® Marine-595

Self-leveling 2-component PUR resin with low thermal conductivity / density

Sikafloor® Marine-595 is a self-leveling aliphatic 2-component polyurethane decorative floor resin, part of the Sikafloor ® Marine
Deco systems.  

  • Low thermal conductivity
  • Low density
  • Cool feeling
  • Permanently elastic
  • Very high yellowing resistance
  • Solvent-free (ISO 16001-6)
  • Very low VOC emission
  • Solvent-free
  • Very good working characteristics
 
Product Data Sheet Show all documents

PRODUCT BENEFITS

  • Low thermal conductivity
  • Low density
  • Cool feeling
  • Permanently elastic
  • Very high yellowing resistance
  • Solvent-free (ISO 16001-6)
  • Very low VOC emission
  • Solvent-free
  • Very good working characteristics
 

Usage

Sikafloor® Marine-595 is designed as part of Sikafloor® Marine Deco systems as synthetic teak decking solution with patented Sika Cool Technology, for external decks in shipbuilding, cruise and leisure boat construction. This product is suitable for experienced professional users only. Tests with actual substrates and conditions have to be performed ensuring adhesion and material compatibility.  

Packaging

Sikafloor® Marine-595 (A)

Container

8.2 kg

Sikafloor® Marine-595 (B)

Container

5 kg

Product Details

Typical Product Data
Properties

Sikafloor® Marine-595 (A)

Sikafloor® Marine-595 (B)

Chemical base

Polyurethane

Isocyanate

Color (CQP001-1)

 

mixed

Colored

Transparent

Various colors available (see color design chart)

Density

 

mixed

0.86 kg/l

1.16 kg/l

0.97 kg/l

Solid content

100 %

Mixing ratio

by weight

41 : 25

Application temperature

substrate / climate

15 ─ 30 °C A, B

Shore A hardness (CQP023-1 / ISO 48-4)

90

Tensile strength (DIN 53504)

8.5 MPa

Elongation at break (DIN 53504)

50 %

Pot-life

15 °C

20 °C

30 °C

150 minutes

100 minutes

70 minutes

Shelf life

9 months C

12 months C

CQP = Corporate Quality Procedure

A) Substrate must be 3 °C above the dew point

B) max. 80 % r.h.C) stored in sealed container in up-right position in a dry place between 5 and 30 °C, protected from direct sunlight
Technical Information

CURE MECHANISM

The curing of Sikafloor® Marine-595 takes place by a chemical reaction of the two components.
Higher temperatures speed up and lower temperatures slow down the curing process.

CHEMICAL RESISTANCE

For advice on chemical resitance contact the Technical Department of Sika Industry.

Application

Application Information

Surface preparation

Sikafloor® Marine-595 is installed on top of the primary deck covering or leveling compound such as SikaTransfloor®-352 or Sikafloor® Marine-530. In case of Sika®Transfloor-352, the top layer must be sanded and the gloss finish needs to be removed. All dust, loose and friable material must be completely removed from the surface before application of Sikafloor® Marine-595.

The application area must be protected against weather to fulfill referenced substrate and climatic conditions.

Application

For deeper sections (e.g. unevenness), it might be necessary to pre-level these in advance and let it cure before flooring process. Sikafloor® Marine-595 is poured and spread evenly to the desired thickness by means of a notched trowel or pinrake. In critical areas a spike roller can be used to improve levelling. Always consider the pot life to keep a wet edge.

Prior to application, always consult the most current corresponding Application Manual.

 

Curing

Indication regarding curing details see table below:

Tempera-
ture

Foot traffic

Light trafficA

Full cure

15 °C

16 hours

32 hours

48 hours

20 °C

12 hours

16 hours

48 hours

30 °C

8 hours

12 hours

24 hours

A) food trolleys and light rolling equipment on soft wheels

Removal

Uncured Sikafloor® Marine-595 can be removed from tools and equipment with Sika® Colma Cleaner or another suitable solvent. Once cured, the material can only be removed mechanically.

Hands and exposed skin shall be washed immediately using hand wipes such as Sika® Cleaner-350H or a suitable industrial hand cleaner and water.

Do not use solvents on skin.

Application limits

Freshly applied Sikafloor® Marine-595 must be protected from damp, condensation and water for at least 1 day. Uncured material reacts in contact with water (foaming).During application, care must be taken that no drops of sweat get onto the fresh Sikafloor® Marine-595 coating (wear sweat bands).

Refer to corresponding Application Manual.

STORAGE CONDITIONS

Both components of Sikafloor® Marine-595 have to be kept between 5 °C and 30 °C in a dry place. Do not expose it to direct sunlight. After opening of the packaging, the contents need to be protected against moisture.

Minimum temperature during transportation is 5 °C.

Documents