Sikafloor® MultiDur ET-14 ECF
Sikafloor® MultiDur ET-14 ECF is a two part, orange peel textured, coloured, electrostatically conductive epoxy flooring system.
- Electrostatic conductive
- Good chemical and mechanical resistance
- Slip resistance
- Easy to clean
- Economical
- Liquid proof
- Total solid
Systemstruktur
Anwendung
It is used as:- Decorative and protective, electrostatic, conductive, textured system for concrete or cement screeds with normal up to medium heavy wear.
- Suitable as a wearing course in industries, such as automotive, electronics and pharmaceutical manufacturing, storage facilities and warehouses.
- Particularly suitable for areas with sensitive electronic equipment e.g. CNC machinery, computer rooms, aircraft maintenance sheds, battery-charging rooms and areas subjected to high explosion risks etc.
Vorteile
- Electrostatic conductive
- Good chemical and mechanical resistance
- Slip resistance
- Easy to clean
- Economical
- Liquid proof
- Total solid
Verpackung
Please refer to individual Product Data Sheet.
Farbsystem
Almost unlimited choice of colour shades. Due to the nature of carbon fibres providing the conductivity, it is not possible to achieve exact colour matching. With very bright colours (such as yellow and orange), this effect is increased. Under direct sun light there may be some discolouration and colour variation, this has no influence on the function and performance of the coating.
Aussehen System
Orange peel textured, semi-gloss
Systemdetails
PRÜFZEUGNISSE
- Textured, high-build coloured epoxy resin coating according to EN 1504-2: 2004 and EN 13813, DoP 02 08 01 02 014 0 000010 2017, certified by Factory Production Control Body No. 0921, certificate 2017, and provided with the CE-mark.
- Varnishability test according to VW-standard PV 3.10.7 (paint wetting impairment substances (PWIS)) like silicones, HQM GmbH, Test Report 14-04-14201871-6, April 2014
- Slip resistance acc. DIN 51130, Roxeler Baustoffprüfstelle, Test Report Nr. 020109-15-6, May 2016
Systemaufbau
Sikafloor® MultiDur ET-14 ECF:
1. Primer + Earthing connection | Sikafloor®-156/-160/-161+ Sika® Earthing Kit |
2. Conductive primer | Sikafloor®-220 W Conductive |
3. Final conductive coating | Sikafloor®-262 AS N Thixo |
The system configuration as described must be fully complied with and may not be changed.
Chemische Basis System
Epoxy
Nenndicke System
~ 0.6 - max. 0.8 mm
Lagerfähigkeit
Please refer to individual Product Data Sheet.
Lagerbedingungen
Please refer to individual Product Data Sheet.
Shore-Härte (D)
~ 77 | (3 days / +23 °C) |
Abriebfestigkeit
~ 100 mg (CS 10/1000/1000) | (7 days / +23 °C) |
Druckfestigkeit
~ 80 N/mm² | (28 days / +23 °C) |
Reißfestigkeit
~ 40 N/mm² | (28 days / +23 °C) |
Brandverhalten
Efl | (EN 13501-1) |
Chemische Beständigkeit
Resistant to many chemicals. Contact Sika technical service for specific information.
Thermische Beständigkeit
Exposure* | Dry heat |
Permanent | +50 °C |
Short-term max. 7 d | +80 °C |
Short-term moist/wet heat* up to +80 °C where exposure is only occasional (i.e. during steam cleaning etc.)
*No simultaneous chemical and mechanical exposure.
USGBC LEED Bewertung
Conforms to the requirements of LEED EQ Credit 4.2: Low-Emitting Materials: Paints & Coatings SCAQMD Method 304-91 VOC Content < 100 g/l
Rutschhemmung
R9 | (DIN 51130) |
Elektrostatisches Verhalten
Resistance to ground1 | Rg < 109 Ω | (IEC 61340-4-1) |
Typical average resistance to ground2 | Rg < 106 Ω | (DIN EN 1081) |
1 In accordance with IEC 61340-5-1 and ANSI/ESD S20.20.
2 Readings may vary, depending on ambient conditions (i.e. temperature, humidity) and measurement equipment.
Anwendung
Lufttemperatur
+10 °C min. / +30 °C max.
Relative Luftfeuchtigkeit
80 % r.h. max.
Taupunkt
Beware of condensation!
The substrate and uncured floor must be at least 3 °C above dew point to reduce the risk of condensation or blooming on the floor finish.
Untergrundtemperatur
+10 °C min. / +30 °C max.
Wartezeit zwischen den Arbeitsgängen
Before applying Sikafloor®-220 W Conductive on Sikafloor®-156/160/161 allow:
Substrate temperature | Minimum | Maximum |
+10°C | 24 hours | 4 days |
+20°C | 12 hours | 2 days |
| +30°C | 8 hours | 1 days |
Before applying Sikafloor®-262 AS N Thixo on Sikafloor®-220 W Conductive allow:
Substrate temperature | Minimum | Maximum |
+10°C | 26 hours | 7 days |
+20°C | 17 hours | 5 days |
| +30°C | 12 hours | 4 days |
Times are approximate and will be affected by changing ambient conditions particularly temperature and relative humidity.
Wartezeit bis zur Nutzung
Temperature | Foot traffic | Light traffic | Full cure |
+10°C | ~ 30 hours | ~ 5 days | ~ 10 days |
+20°C | ~ 24 hours | ~ 3 days | ~ 7 days |
+30°C | ~ 16 hours | ~ 2 days | ~ 5 days |
Note: Times are approximate and will be affected by changing ambient conditions
Materialverbrauch
Coating | Product | Consumption |
Primer | Sikafloor®-156/-160/-161 | 1-2 x ~ 0.3 - 0.5 kg/m² |
Levelling (if required) | Sikafloor®-156/-160/-161 levelling mortar | Refer to PDS of Sikafloor®-156/-160/-161 |
| Earthing connection | Sika® Earthing Kit | 1 earthing point per approx. 200 -300 m², min. 2 per room. |
| Conductive primer | Sikafloor®-220 W Conductive | 1 x 0.08 - 0.10 kg/m² |
Final conductive coating | Sikafloor®-262 AS N Thixo | 1 x 0.75 kg/m² |
These figures are theoretical and do not allow for any additional material due to surface porosity, surface profile, variations in level or wastage etc.
CLEANING
Please refer to the Sikafloor® Cleaning Regime.